Steam explosion is one of the most effective pretreatment for fractionating wood. This leads to the total utilization of wood basic components; cellulose, hemicellulose and lignin. The amount of sugar and lignin extracted with the hot water method was very low. The lignin content of residues after extraction with using a sodium hydroxide treatment, increased delignification of carbohydrate as the concentration of alkali was increased. Oak, pretreated with steam exploded at 25kg/$cm^2$ for 6 min. then 1% alkali for 2hrs. showed a delignification rate up to 95%. A sodium chlorite treatment of steam exploded pine and oak also afforded a high deligninfication effect. Pine, treated 10% sodium chlorite for 2hrs. showed high delignification. However, by using a sodium hydroxide treatment, a 2% retreatment for Ihr. after a 2% for 2hrs. afforded remarkable delignification effect on exploded wood at 30kg/$cm^2$ for 9min. and at 35kg/$cm^2$ for 3-6min. In oak, an initial 2hrs. treatment of 2% sodium chlorite was followed by a second 2hrs. treatment at 10%. This showed a delignification rate of 96%.