This research was carried out to investigate the effects of cyclic humidification on the dimensional stability of particleboard manufactured according the three specific gravity levels and com-ply fabricated with a core of particleboard and veneer or plywood as the face and back materials. Both the particleboard and com-ply were subjected to four cycles of 50-90-50% relative humidity. The results are summarized as follows: Particleboard and com-ply followed a clear pattern of increasing dimensions and weight on the adsorption cycle and decreasing dimensions and weight on the humidification cycle. After the fourth cycle, the dimensions and weight of both particleboard and com-ply were greater than those originally measured. The greater part of increase in occurred during the first humidification cycle. The specific gravity of particleboard has a significant effect thickness and volume change. The dimensional stability of com-ply was better than that of particleboard. In addition, the dimensional stability of com-ply bonded with plywood was better than that of com-ply bonded with veneer.