Japanese red pine (Pinus densiflora S. et. Z.) decayed by brown-rot fungi Tyromyces palustris and Gloeophyllum trabeum were subjected to X-ray diffraction analysis and infrared spectral examinations. Pine woods decayed by T. palustris showed the increase of relative crystallinity in the initial stage of degradation. When the weight loss was above 30%, then the crystallinity went down slowly. In contrast, the wood samples degraded by G. trabeum showed the decrease of crystallinity from the beginning stage of decay. The changes of crystallinity in brown-rotted woods suggested that the degradation rate of crystalline cellulose was varied with the brown rot fungal species. X-ray diffraction analyses also indicated that crystalline cellulose was much more slowly broken down than the amorphous one. The most notable difference in the IR spectra of the brown-rotted wood samples was that the adsorption band centered at 1,730$cm^{-1}$ was significantly diminished in the decayed wood. indicating the degradation of hemicellulose by brown-rot fungi. However, no marked changes of intensities at 1,000, 1,060 and 1,040$cm^{-1}$ were observed in the brown rotted wood samples, suggesting that crystal line cellulose was resistant against the attack by brown rot fungi.