This study was aimed at resolving uncertainties about lamellar tearing initiation temperatures and studying the effect of nonmetallic inclusions on the tear initiation. In order to measure the lamellar tearing initiation temperature, the slice bend test was conducted in the temperature range of 20.deg.C to 425.deg.C on A572 Grade 50 and A588 Grade A steels. In addition, the weld restrain test was carried out to measure directly the tear initiation temperature with A572 steel. In slice bend tests, A572 steel showed the most susceptible region to lamellar tearing to be in the range of 100 to 300.deg.C, where the steel showed the minimum ductility. The observed tear initiation by the weld restraint test was to be in the range of 200to 300.deg.C. The tears became narrower and less rounded at the susceptible temperatures. It was confirmed in this study that lamellar teraring initiated during cooling from welding in the range of 200 to 300.deg.C and they were initiated by strain aging embrittlement.