Most degeneating diseases and back pains in the orthopaedic disease are originated from the unbalance of stress distribution in the low-lumbar spine. Therefore the stress analysis of lowerback is indispensible to the clinical diagnosis for the developing reason and the developing process of diseases. Therefore the same model materials as following are eveloped to analyze the stress distributions of lower-back by photoelastic experiment. The verterbral body and the process are molded from epoxy resin(the weight ratio of Araldite and hardner is 10 to 3), models are geometrically identical to them in vivo respectively and the ratio of their elastic modulus to that of model material is 1 to 10. It is assured that KE-1300 Silicon(E=0.8MPa), TSE-3562 Silicon(0.5MPa) and the composite silicon(3MPa) (the weight ratio of KE-1300 silicon and Jioreal : 10 to 4) are respectively effective as the model materials of ligament, musles and intervertevral disc which is essential to the movement of low-lumbar spine. All the elements associated with the movement of the low-lumbar spine are molded through the molding method developed in this research and assembled with the angles between the verterbra and the disc in the normal human lumbosacral spine. The stress distributions of the assembled model are analyzed by photoelastic experiment. It is certified by comparing the results of photoelastic experimebt with the clinical situations that the loading dveice and the loading conceptions used in this paper are effective.