We have investigated the effects of sputtering Ar gas pressure on magnetic and magneto-optical properties in compositionally modulated Co/Pd superlattice thin films. The samples were prepared by dc magnetron sputtering from 2-in.-diam Co and Pd targets by alternately exposing the substrates to targets. Sputtering Ar gas pressure was varied from 2 to 30 mTorr. All samples had same bilayer thicknesses composed of 2-$AA$-thick Co and 9-$AA$-thick Pd sublayers. It was observed that the colum-nar structure was more distinctively developed with increasing Ar gas pressure. We observed that the intrinsic uniaxial anisotropy energy, magnetization and polar Kerr rotation were decreased with increasing Ar gas pressures. Large coercivity and perfect squareness were attained by the deposition at the high Ar gas pressure. We believe that the results are mainly ascribed the variation of micro-structure with sputtering Ar gas pressure.