Experiment has been performed to investigate the thermal and magnetic properties of Mn-ferrite by electrolysis. Using the 0.2%C mild steel as soluble anode and SUS 304 stainless steel as cathode, Mn-ferrite could be made from the sulfuric acid leaching of the wasted manganese dry cell and $MnSO_4$reagent by electrolysis. As the result of X-ray diffraction, thermal analysis and magnetic measurement, Mn-ferrite was the spinel type in $Mn_{x}Fe_{3-x}O_4$ (X=1), the weight loss rate of $Mn_{x}Fe_{3-x}O_4$ were linearly increased up to the $200^{circ}C$. Ms, Mr and Hc values were decreased with increasing Mn content and heating temperature. When Mn-ferrite was formed by $MnCl_2$reagent electrolysis, Ms values were higher than those formed from the sulfuric acid leaching of the wasted manganese dry cell and $MnSO_4$reagent by electrolysis. In Mn-ferrite, which was formed from the sulfuric acid leaching of the wasted manganese dry cell by electrolysis, Ms and Mr values were higher, Hc values were lower than which was formed by $MnSO_4$ reagent electrolysis at $200^{circ}C;and;300^{circ}C, while the same values at $100^{circ}C$. The shape of particles was spherical type, the sizes of them were about $0.1{mu}m$ sub-micron in $MnSO_4$reagent electrolysis, $0.5{mu}m$ in the sulfuric acid leaching of the wasted manganese dry cell by electrolysis.