Annealing effects on the permeability aftereffect(disaccommodation) of liquid quenched single strip $Fe_{73.5}Cu_1Nb_3Si_{16}B_{6.5}$ alloys were investigated with pulse method. The initial susceptibility X, $B_{10},$ (the flux density at 10 Oe) and disaccommodation intensity D (D = [X(1 s)-X(64 s)]/X(1 s), where X(1 s) and X(64 s) are the susceptibility of 1 and 64 s of rest time after A. C. demagnetization) were about 800, 0.8 T and 16 %, respectively. The soft magnetic properties were improved with isothermal annealing for 1 hour at $300{sim}600^{circ}C.$ X, $B_{10},$ and D at $570^{circ}C$ of optimum annealing temperature were 15000, 1.2 T and 1.1 %, respectively. The origin of the change of characteristics were examined with fine crystalline structure and magnetostriction.