Glass ceramics for crown were prepared by adding 3$sim$11 wt% TiO2 to the weight percent composition of 34.7 CaO, 27.8 SiO2, 18.3P2O5, 12.6MgO and 6.6 TiO2. The starting glasses were prepared by melting the powdered batch in alumina crucible at 1350$sim$1400 for 1 hr and then quenching into a distilled water. The nucleation and crystallization of the crystalline glass ceramics for crown were studied by DTA, SME and X-ray diffraction analysis. Frit containing 9.11 wt% TiO2 had crystallization temperature of 850$sim$1075 and major crystalline phase was identified by X-ray diffraction as diopside(CaO-MgO-2SiO2). Activation energies for the crystallization processes were obtained from DTA by varing rates for the fits, and were calculated from modified Ozawa and Kissinger equations. Activation energy for the crystallization processes of the S-4 frit was 489.6 KJ/mol.