The phenol resorcinol formaldehyde resin (PRF) adhesives which are curing at ambient temperature for structural purposes were synthesized. A PRF resin is produced according to the two-stage reaction system. In first stage, a low-condensed resol or methylolated phenol were prepared from phenol by reaction with a formaldehyde in alkaline condition. The molar ratio of phenol to formaldehyde was 1.0~1.4. And in second-stage, resorcinol was added to combine with the methylol group of a low-condensed resol(R/P molar ratio 0.3). The glue-joint strength, pot-life and workability of this synthetic PRF resin were superior to conventional ambient temperature setting adhesives such as oilic urethane or water based polymer-isocyanate resin for wood adhesives.