Na-Fe Tourmalene ($NaFe_3Al_6B_3Si_6O_{27}F_4$)single crystals were grown by FZ method. The Growth conditions are counter rotation 20~30rpm, growth rate 1~5mm/hr in the atmospheric environment. The transition elements as Fe(in this research), Mn, Co, etc, are exist in the theoretical fomulae so that dopants were not added. The feed rod was sintered between $1000^{circ}C$ and $1l00^{circ}C$, but at higher temperature, it was difficult to manufacture the feed rod because of evaporation of the elements such as F. As grown crystals had a black color and the length of 50~60mm, the diameter of 5~6mm. X-ray powder diffraction pattern indicated that the composition of the feed rod was right to the Tourmaline composition. By FT-IR spectra, the state of bonding of each element was charaterized.