In joining alumina ceramics to metal by using Mo-Mn metallizing process the effects of metallizing thickness, temperature, and the composition of paste on the bond strength and the microstructure of joining interface were investigated. The bond strength variation in the range of metallizing temperature, 1350~155$0^{circ}C$ was more than 150MPa above 145$0^{circ}C$ and the optimum metallizing thickness was 30${mu}{ extrm}{m}$. The optimum contents of Mn in Mo-Mn paste was 5% due to the bond strength decrease with the increase of addition. The effect of SiO2 addition in paste on bond strength was saturated around 200MPa. It was also observed that as the particle size of Mo decreased, the joinning with higher bond strength was shown in spite of low metallizing temperature.