In order to analysis creep characteristics and elastic recovery of the high-tech fibers for fishing gear materials, creep and elasticity tests were carried out on netting twines made of nylon, kevlar 29 and techmilon respectively. After creep tests, the rupture surface of raw materials was observed by scanning electron microscope(SEM). The results obtained are as follows: 1. Netting twines were arranged in order of creep rupture time as follow: techmilon, kevlar 29, nylon. The creep progressive pace was the fastest in techmilon. 2. In order of the creep elongating, netting twines were arranged as follows: nylon, techmilon, kevlar 29. 3. The rupture time T sub(r) decreased almost linearly with the increase of applied load L on the log-log scaled graph. The empirical equations computed for kevlar 29 and techmilon are as follows: T sub(r kevlar 29)=1.9512$ imes$1037L super(-15.773). T sub(r techmilon)=2.7146$ imes$1016L super(-6.831). 4. It was observed by SEM that creep was progressed in all netting twines. The difference of rupture morphology was recognized clearly in tensile and creep tests. 5. In order of the elastic recovery, netting twines were arranged as follows: techmilon, kevlar 29, nylon.