The preparation of $TiO_2$ fine particles from $TiCl_4$ and oxygen by the vapor-phasereaction was investigated at $850^{circ}C$ with an emphasis on the effect of its experimental conditions on the crystal type of the products. Anatase $TiO_2$ particles prepared by experiment were used to study anatase-rutile transition by calcination temperature, the additives and gas atmosphere. The results were as follows. The kinetics of anatase-rutile transition was well agreed with A vrami equation, and the activation energy of transition was 35kcal/mol. The addition of CuO in anatase $TiO_2$ particles accelerated the anatase-rutile transition, and its transition was retarded in vaccum.