The purpose of this study was to evaluate the effect on treatment methods to shear bond strength between composite resin and amalgam when the alloy surface was finished with a diamond wheel or an sandblaster. Forty round acrylic cylinders were fabricated with a diameter of 33mm and a height of 20mm to fit into the device used during shear bond strength testing. A round undercut cavity (diameter, 8mm: depth, 2.5mm) was prepared in the center of the acrylic surface and the cavity was restored using a amalgam. A total of 40 acrylic cylinders with amalgam were divided into 4 groups according to treatment method. The group treatment were as follows : Group 1 : acid etching after finishing the amalgam with diamond wheel Group 2 : no acid etching after finishing the amalgam with diamond wheel Group 3 : acid etching after sandblasting the amalgam Group 4 : no acid etching after sandblasting the amalgam The shear bond strength of composite resin bonded to amalgam of each specimen was tested with a universal testing machine at a crosshead speed of 0.5mm/min and 500kg in full scale. The results were as follow: 1. After diamond finishing, the non-acid etching group had highest shear bond strength with 7.29kg/$cm^2$ and after sandblasting, the acidetching group had lowest shear bond strength with 4.49kg/$cm^2$. 2. In both diamond finishing and sandblasting group, acid etching of the roughened amalgam surface decreased the shear bond strength. 3. The group treated with a diamond wheel had higher shear bond strength those treated with an sandblaster but there was not significanat.