To provide further information for reutilization of the waste wood obtained after cultivating oak mushroom in Kangwon-do, the crystal structures of the waste wood were investigated and compared to those of normal woods by a series of x-ray diffraction analysis. The results obtained are as follows: 1. An x-ray diffraction diagram of cultivated wood for 5 years was same as that of typical cellulose with some orientation of cellulose crystallites, but that of cultivated wood for 8 years a random. 2. Crystallinity indices in normal and cultivated woods for 5 years ranged from 57% to 60%. In the cultivated wood for 8 years, however, the value showed about 40%. 3. Crystallite widths of cultivated woods for 5 years and for 8 years were 3 nm and 2.5 nm, respectively. 4. Intensity ratios of equatorial and meridional layers did not show any significant differences. From the above results, it is clear that the waste wood obtained after cultivating oak mush room for 5 years showed basically same crystal structures with normal wood. Therefore, we think that the waste wood may be used available for cellulosic material instead of normal wood.