정온발열 특성을 갖는 PTC 써어미스터를 사용하여 유속센서를 제조하였다. $(Ba_{0.7}Sr_{0.3})TiO_{3}$ 분말을 사용하여 PTC 써어미스터를 제조한 후, 유속에 따른 저항률의 변화를 조사하였다. 유속이 0 cm/s에서 5 cm/s로 변할 경우 저항률은 4.45 $k{Omega}{cdot}cm$에서 3.95 $k{Omega}{cdot}cm$로 변하였다. 유속이 1 cm/s와 5 cm/s일 경우 PTC 써어미스터의 감도는 -204 (${Omega}{cdot}cm$)/(cm/s)와 -24 (${Omega}{cdot}cm$)/(cm/s)로 나타났다.
Flow sensor was fabricated with PTC thermistor usually operating as thermostats. The PTC thermistor was manufactured with $(Ba_{0.7}Sr_{0.3})TiO_{3}$ powder and its resistivity as a function of flow velocity was investigated. The resistivity changed from 4.45 $k{Omega}{cdot}cm$ to 3.95 $k{Omega}{cdot}cm$ as flow velocity varied 0 cm/s to 5 cm/s The sensitivities of the PTC thermistor were -204 (${Omega}{cdot}cm$)/(cm/s) and -24 (${Omega}{cdot}cm$)/(cm/s) at the flow velocity of 1 cm/s and 5 cm/s, respectively.