Growth form and surface morphology of NYAB single crystal grown by TSSG technique using a K2O/3MoOS/0.5B203 flux was investigated. In the crystal grown from <100> or <120> seed, prismatic and (101) faces were well developed with different size each other. (001) face was also developed in the crystal grown from <001> seed. While growth hillocks were observed on the prismatic face of the crystal grown from <100> seed, surface striations parallel to neighbor (101) faces were formed on that face of the crystal grown from <001> seed. The (101) faces were grown by two dimensional nucleation growth. (001) face which was developed at slow growth velocity of [001] direction was grown by screw dislocation Anisotropy of growth velocity as to seed orientation affected on crystal morphology and surface morphology.