This study was performed to evaluate the engineering properties of the lightweight concrete using surlightweight aggregate foaming agent and high performance agent. The following conclusions were drawn. 1. The unit weight of type A, B and C concrete was 0.912t/m$^3$, 1.592t/m$^3$ and 1.070t/m$^3$, respectively. Specially, the unit weight of type A concrete was decreased 42% than that of the type B concrete. 2. The highest engineering property was measured in the lightweight concrete using high performance agent Also, the ratio of tensile and bending strength to compresive streng-th of the lightweight concrete was higher than that of the normal cement concrete. 3. The dynamic modulus of elasticity of the lightweight concrete was in the range of 2.86 x 10 5~9.86 x 10 5 kg/cm$^2$ which was approximately 300% than that of the normal cement concrete. 4. The ultrasonic pulse velocity of the lightweight concrete was in the range 2047~3394 n/sec, which was smaller than that of the normal cement concrete.