Transparent, crack-free dried gel monoliths with a composition of LiZr1.5Si2P2O12.5 have been synthesized by the low temperature polymerization of the Sol-Gel technique using metal alkoxides as starting materials. After initial reaction (20~40 min), each metal alkoxide closely paralleled each other during the hydrolysis reactions. The safe drying conditions of gels with no creaks the control of the shrinkage rate. The gels converted into the glass by heat treatment at 75$0^{circ}C$. FTIR data indicated that the gels were phase separated into silicarich and phosphate-rich regions with the lithium. XRD results showed the formation of crystalline LiH2PO4. The gels dried at 15$0^{circ}C$ or fired at 75$0^{circ}C$ contained the residual water. The high ionic conductivity at room temperature for these gels was attributed to the motion of protons.