BaTiO3 ceramics doped with 0.1 to 4.0 mol% Nb2O5 were prepared by conventional solid stage sintering process, so as to investigate the effect of the amount of Nb2O5 on the dielectric properties and complex impedance patterns of barium titanates. From the measurement of capacitance, we found that the dielectric constant of BaTiO3 samples with 1 mol% or more Nb2O5 remained approximately constant around room temperature with values higher than 2500. In this paper, the effect of impurity content as well as temperature on complex impedance patterns was discussed in detail. In particular, the grain and grain boundary behavior of samples which showed PTCR characteristics was discussed in terms of measuring temperature.