Tape casting technique was successfully applied to produce porous ceramics and multi-layered ceramics containing porous layers, where spherical hollow polymer particles were introduced as pore precursors. In the presence of extreme differences in density and size between Al2O3 and pore precursor particles, hindered settling was effective in preventing segregation of component particles and packing behavior of mixed powders was improved through bimodal packing. There were two transitions in packing behavior of mixed powders. The first transition took place at 40~50 vol% pore precursor addition, where majority of pores changed from close to open pore state. The other transition occured at 60~70 vol% pore precursor addition, where pore precursor particles formed a continuous network structure.