The effects of the dispersion, drying, and binder burning-out on the green-microstructures of gelcasted alumina were studied. The slip consisting of 55 vol% alumina powder and 5 wt% organic materials was well-dispersed by adding 0.28 wt% polyelectrolyte polymer. Green bodies were dried at >85% relative humidity at room temperature. Green-microstructures were observed to be depended on the heating rate during binder burnout. Constant drying rate was not observed in drying process of gelcasted alumina. Sintered body showed its relative density higher than 99% when it was sintered at 1$600^{circ}C$ for 2 hours.