A bilayer film consisting of a layer of a-Se$_{75}$ Ge$_{25}$ with a surface layer of silver -100[.angs.] thick and a monolayer film of a-Se$_{75}$ Ge$_{25}$ are irradiated with 9[keV] Ga$^{+}$ ion beam. The Ga$^{+}$ ion (10$^{16}$ [ions/cm$^{2}$] exposed a-Se$_{75}$ Ge$_{25}$ and Ag/a-Se$_{75}$ Ge$_{25}$ thin films show an increase in optical absorption, and the absorption edge on irradiation with shifts toward longer wavelength. The shift toward longer wavelength called a "darkening effect" is observed also in film exposure to optical radiation(4.5*10$^{20}$ [photons/cm$^{2}$]). The 0.3[eV] edge shift for ion irradiation films is about twice to that obtained on irradiation with photons. These large changes are primarily due to structural changes, which lead to high etch selectivity and high sensitivity.