According to spread volume of B(BiPbCuO) layer, composition ratio and each stage of sintering process, we studied stability of high Tc superconductor phase and generation and growth movement of superconducting phase. The dual layer composed of SrCaCuO and BiPbCuO compound were prepared to develop the Bi-2223 superconductor[108K] through interaction and diffusion during sintering process. The dual layer samples were sintered at 830.deg. C for 0-210 hours. From the result, the optimum conditions were : spread volume(A:B=1:0.6), sintering time(210h) and composition ratio(A:S $r_{2}$C $a_{2}$C $u_{2}$- $O_{x}$, B:B $i_{1.9}$P $b_{0.5}$C $u_{3}$ $O_{y}$) at 830.deg. C.. C.C.C.