In this study, ferroelectric thin films of PZT with different Zr/Ti ratio were prepared by sol-get processing and annealed by rapid thermal annealing at >$500^{circ}C$>$-700^{circ}C$</TEX> for 10 sec. -1 min. Structures of the annealed films were examined by X-ray diffraction and SEM. Thin films of PZT with perovskite structure have been obtained by annealing at >$600^{circ}C$ or above and for 20 seconds or longer. Maximum remnant polarization of 10.24.mu.C/cm$^{2}$ and minimum coercive field of 20.06 kV/cm were obtained from the 56/44 and 65/35 Zr/Ti composition films, respectively. Dielectric constant, .epsilon.$_{r}$ of 500-1300 and dielectric loss, tan .delta., of 0.01-0.035 were obtained from the films.s.