This study was conducted to develop the long-tenn storage method to minimize the black spot occurred on the surface of persimmons stored in the films at low temperature. The storage experiments were done with different films and persimmon varieties at $0^{circ}C$ storage condition for 5 months, and then the physical and chemical characteristics of persimmons were tested monthly. The results were as follows : 1. The film 160 made from zeolites showed highest performance in well storings sweet persimmons for 5 months, compared with other films by eyesight. The initial moisture condensation inside the films seemed to cause the black spots on persimmons, and the effect of the film holes was never significant to prevent the black spots. 2. The sugar content was ranged from $14^{circ}Brix$ to $15^{circ}Brix$ regardless of film types and persimmom varieties, and it changed little for storage of 5 months. 3. The decrease rate of persimmom weight in the film 160 and 180 was 0.3% for storage of 5 months, while those in other films reached to 2%. The decrease rate of persimmon weight was least in the film 160 and 180. 4. The hardness of Fuyu least decreased in the films 160 and 380. It was changed from 36 kg/cnf to 8-27 $kg/cm^2$, and that of Charyang was from 31 $kg/cm^2$ to 8-10 $kg/cm^2$ for storage of 5 months. The hardness of Charyang rapidly decreased as storage period increased. 5. The average rate of black spot(defect rate) of Fuyu measured by a computer image processing system was least in the film 160 by 0.5%, but those in other films was ranged from about 5% to 20% for storage of 5 months. The rate of black spot of Charyang was less than that of Fuyu among most of films. 6. The intensity, hue, and saturation in persimmon color changed according to storage period. Especially, the intensity of persimmon colors decreased as storage period increased, but it was least in the film 160. 7. An integrated long-term storage method of sweet persimmons was suggested in the basis of the experiments and literature reviews.