The structure and mechanical properties of the extruded specimens were investigated in rapid solidified Al-(1, 3, 5) Cr alloys after mechanical alloying. Finer lamellar microstructure could no longer be resolved in the bars obtained by extrusion of the spherical particles after 200 min. of processing time. The structure of extruded bars are highly depended on the processing time of splats. The isothermal annealing of the extruded bars showed that all the alloys had good thermal stability up to $400^{circ}C$ and did not show the recrystallization phenomena. Severe working of Al-(1, 3, 5) Cr splats produced a very fine grain size and substructural strengthening (high dislocation density and fine grain size). Effects of mechanical alloying on the thermal stability of the extruded bars Al-(1, 3, 5) Cr alloys decreases, with increasing Cr content. But the ultimate tensile Strength in the extruded bars increases with increasing Cr content.