A coprecipitation method was used for preparing Ca and Pt doped $SnO_{2}$-based material. Crystallite size and specific surface area were investigated by TEM, XRD and BET analysis. $SnO_{2}(Ca)/Pt$ based thick film devices were prepared by a screen printing technique for hydrocarbon gas detecting. Then the electrical and sensing characteristics of devices were investigated. As Ca and Pt addition, the crystal growth of $SnO_{2}$ was suppressed during calcining and sintering, and the sensitivity of $SnO_{2}(Ca)/Pt$ thick film to gas was enhanced. Also any difference in the sensing properties has to be attributed to the Pt and Au electrode. For the 2000 ppm $CH_{4}$, the sensitivity of $SnO_{2}(Ca)/Pt$ thick film devices were about 83% at an operating temperature of $400^{circ}C$.