The possibility of new GMAW process using economic shielding gases including CO$_{2}$ gas was investigated on the effect of shielding gas on weldabilty. In the optimum welding condition using 600A power source, FCAW process showed low depositions rate, 114 g/min at 300A, but new GMAW using other mixed shielding gases exhibited high deposition rate, 208-224 g/min at 450A. TIME gas, Ar+CO$_{2}$ gas and Ar+CO$_{2}$+O$_{2}$ gas as a shielding gas were able to be used to the very high welding current(450A), moreover TIME gas and Ar+CO$_{2}$ gas showed the highest arc stability among shielding gases studied in this experiments. The weld penetration was performed by axial spray transfer mode of weld droplet. On the basis of workability, weldability and economic point of view, Ar mixture (80%Ar+20%CO$_{2}$) gas was recommended as a shielding gas for the development and application of new GMAW process. This shielding gas showed the low spatter, good weld quality, stable arc and low cost at the region of high welding current.