This study was performed to develop the lightweight concrete using synthetic lightweight aggregate and natural coarse aggregate. Mixing ratios were three types, the first type was mixed cement and synthetic lightweight fine aggregate (Type CP), the second type was mixed cement, synthetic lightweight fine aggregate and synthetic lightweight coarse aggregate (Type CPE), the third type was mixed cement, synthetic lightweight fine aggregate and natural coarse aggregate (Type CPN). The results of this study are summarized as follows ; 1. The W/C of each mixing ratio was increased with increase of the amount of cement used, and it was shown higher in order of Type CP, CPN, CPE. 2. The unit weight of Type CP, CPE and CPN was 1.473~1.647g/cm$^3$, 1.467~1.622g/cm$^3$ and 1.658~1 .838g/cm$^3$, respectively. And the absorption ratio was approximately 20%, which was higher than that of the normal cement concrete. 3. The compressive strength of Type CP was shown 178 ~249kg/cm2, Type CPE was shown 149~241kg/cm$^2$ and Type CPN was shown 196~297kg/cm$^2$, respectively. Each strength ratio was smaller than that of the normal cement concrete. 4. The pulse velocity of Type CP, CPE and CPN was 2, 688~3, 240m/sec, 2, 981~3, 324m/sec and 2, 989 ~ 3, 545m/sec, respectively. And it was increased with increase of strength and unit weight. 5. The length change ratio at 28 days was in the range of 0.057~0.077%, and earlier length change ratio was higher than that of the later.