In recent years, many ceramic researchers have discoved various methods of joining ceramic to metal. However, most of these joining methods are perfomed under vacuum and pressured circumstances. So, when we join ceramic to metal,the proceedings are very complicated and require a very high cost. The purpose of this study is to develop a new joining method of an alumina ceramic to an aluminum metal in air atmosphere. The joining condition, such as copper metallizing, nickel plating, brazing, etc. was investigated through the shear strength test of the trial joint. The results obtained from the above experimenta are summarized as follows : 1) In the case of the $Al_2O_3$/$Al_2O_3$joint, the shear strength of the joint was affected by the various foctor such as kaolin content, copper metallizing thickness, firing temperature, firing time. 2) The better shear strength of the $Al_2O_3$/Al joint was obtained when Ni plating was conducted under higher current density than existing plating condition. 3) The shear strength of the $Al_2O_3$/Al joint increases with the Ni plating thickness is confined to the range of this paper. 4) The shear strength of the thermal-shocked specimen($Al_2O_3$/Al joint) was far more deteriorated than that of the as-bonded specimen.