The effects of surface oxidation on magnetic properties were investigated at high frequencies (10k-100MHz) for $7-18mu extrm{m}$ thick $Co_{70}Fe_{5}Si_{15}B_{10}$ amorphous ribbons with controlled domain structure. Oxidation was accelerated by acid-treatment or anodic oxidation treatment, and the insulation layers were prepared on the surfaces of the ribbons. The acid-treatment was effective in improving permeability and magnetic loss. Although the anodic oxidation treatment was effective in both making oxide layer and thinning, the magnetic properties were not improved compared with the case of the acid-treatment