Blanks of SiCp/Al-Li composite were produced by way of powder explossion consolidation method which has been optimized in parameter thriugh expoeriment. By SEM, it was found that the microstructure of this composite has following characteristics : (1) SiC particles are uniformlu distributed in the composite ; (2) Al-Li powders still remain original dendrite structure ; (3) There is some metalluryical bonding between composite particles ; (4) hine particles deform or milt preferentiallu and along some direction deformation of Al-Li particles ; (5) SiCp/Al-Li composite is composed of two kind of Al-Li pweders with very different size ; (6) press-torsion, pressless sinter and hot is static press treatment will make original dendrite in Al-Li particles disappear, further enlargi metallurgical bonding region and incress the dinsity of composite.