0.15(B $a_{0.95}$ S $r_{0.05}$)O-0.15S $m_{2}$ $O_{3}$-0.7Ti $O_{2}$ ceramics were fabricated by the mixed-oxide method. Microwave dielectric properties were investigated with sintering conditions. Increasing the sintering temperature from 1300 to 1375[.deg. C], the sintered density was increased from 5.44 to 5.63[g/c $m^{3$]. Increasing the sintering temperature, dielectric constant and quality factor were increased and temperature coefficient of resonant frequency was independent of sintering temperature. In the specimen sintered at 1375[.deg. C], dielectric constant, quality factor and temperature coefficient of resonant frequency were 80.79, 2784(at 3[GHz]), +11.07[ppm/.deg. C], respectively..