The electrical properties of (S $r_{0.50}$P $b_{0.25}$B $a_{0.25}$)Ti $O_{3}$ ceramics were studied. Specimens were prepared by the conventional mixed oxide method, and fired between 1300[.deg. C] - 1375[.deg. C], for 2[hr.]. The electrical and structural preperties of specimens were investigated with sintering temperature. Increasing the sintering temperature from 1300[.deg. C] to 1375[.deg. C], average grain size was increased from 2.61[.mu.m] to 4.53[.mu.m]. (S $r_{0.50}$P $b_{0.25}$B $a_{0.25}$)Ti $O_{3}$ specimen sintered at 1350[.deg. C] for two hours showed good dielectric constant(2147) and dielectric loss(1.7[%]) properties at 1[khz]. Sintered density and breakdown field strength were the highest value of 5.75[g/c $m^{3}$], 20[kV/cm], respectively. Dielectric properties with applied voltage were independent of the sintering temperature.temperature.