In this study, the BaTiO$sub$3/ capacitor add to MnO$sub$2/ like depressor and shifter were investigated for temperature or voltage compensation by structural and electrical analysis. The relative density of BCTM, generating poly crystall and formation of lattice defect, has a 90[%] over as the CaTiO$sub$3/ come out to control grain size. The current density of BCTM2 increased non-ohmic in high-electric field but that BCTM3 and BCTM4 had a few changing. The BCTM3 and BCTM4 unformated grain boundary shown temperature compensation properties, so that the dielectric constant was low value. The curie point was near 140[.deg. C] in BCTM1 and BCTM4, but BCTM3 and BCTM4 not shown the curie point. It is found that the charging energy of BCTM4 was changed 6[%] according to rising temperature from room temperature to 417[K]. The formation of BaMnO$sub$3/ was low dielectric constant to change frequency and temperature.