Mn-Zn ferrite thin films were deposited on $SiO_2(1000 AA)/Si(100)$ by ion beam sputtering using a single ion source. A mosaic target consisting of a single crystal(ll0) Mn-Zn ferrite with a Fe metal strip on it was used. As-deposited films without oxygen gas flow have a wiistite structure due to oxygen deficiencies, which originated from the extra metal atoms sputtered from the metal strips during deposition. The as-deposited films with oxygen gas flow, however, have a spinel structure with (111) preferred orientation. The crystallization of thin films was maximized at the ion beam extraction voltage of 2.lkV, at which the deposited films are bombarded appropriately by the energetic secondary ions reflected from the target. As the extraction voltage increased or decreased from the optimum value, the crystallinity of thin films becomes poor owing to a weak and severe bombardment of the secondary ions, respectively. Crystallization due to the bombardment of the secondary ions was also maximized at the beam incidence angle of $55^{circ}$. The as-deposited ferrite thin films with a spinel structure showed ferrimagnetism and had an in-plane magnetization easy axis.