When steels are heated at $1000^{circ}C$ in a fused borax bath containing $V_2O_5$ and $B_4C$powders, vanadium carbide layers are formed on the steel surfaces. Since a decrease in carbon concentration and in microhardness in the substrate just below the carbide layer has been observed, gas nitrocarburizing and vanadium carbide forming processes were combined to form a V(C,N) type layer which prevented the decrease in carbon concentration in the substrate. EPMA analysis was done for this V(C,N) type layer. Hardness just below the layer and wear resistance properties of such treated specimens were investigated.