TEM specimen preparation methods have been examined to characterize Cu oxide particles in the polyimide film. Polyimide films were prepared by coating polyamic acid onto Cu films which had been deposited on TEM-mask and glass substrates and Cu foil, followed by thermal curing. In case of TEM-mask, direct observation was possible without further preparation. In other cases, TEM specimen were made by separating polyimide film from the substrate. Polyimide films were removed from glass and Cu foil by dissolving glass in HF solution and Cu foil in $H_{2}SO_{4}$ solution. TEM-mask observation confirms that fine $Cu_{2}O$ particles precipitate in the polyimide as a result of reaction of polyamic acid with Cu. However $Cu_{2}O$ particle reacts with HF and $H_{2}SO_{4}$ solution during dissolving the substrate and interpretation could be misled. It is concluded characterization of $Cu_{2}O$ particle in polyimide using TEM-mask is better than other methods.