Composite resin repair requires strong bond strength between the new and old materials. The objective of the current study was to identify the optimal treatments for sufficient bond strengths. Bondings between same kinds of materials and cross bondings using chemical curing composites and light curing composites were tested. Surface treatments included the methods of sand-blasting, acid etching and coating of bonding agent. Seven kinds cases of combinations from three kinds of methods were experimented and compared with a control group of which surfaces were highly polished. Measurements of shear bond strength and observations of surface morphologic changes using a scanning electron microscope were done. Following conclusions were drawn : 1. The highest bond strength among composite resins were exhibited by the treatment of the sand-blasting and the coating of bonding agent. 2. Acid etched surfaces showed the lowest bond strength. Bond strengths obtained from experimental groups including acid etching were lower than those obtained from same kinds of experimental groups without acid etching. 3. Simple method of the coating of bonding agent produced the slightly increased bond strength on chemical curing composite and reduced bond strength on light curing composite. 4. Bonding surfaces of chemical curing composite resin showed slightly higher bond strengths than light curing composite resin, however significant differences were not confirmed statistically. 5. More significant irregular surfaces were created by sand-blasting method than acid etching method. 6. A principal component of fillers of both resins was silicon. Acid etching method produced the seperations and degradations of fillers, these were significant on light curing composite resins which containing barium fillers.