The purpose of this study is to evaluate the color differences in the In-Ceram according to coping thickness and various abutment core materials ; amalgam, precious alloy, composite resin, non-precious alloy. After the porcelain was built up on the In-Ceram coping at the thicknes of 0.3mm and 0.5mm then it was cemented with glass ionomer cement to the post & core materials. The following results were obtained. 1. There were significant differences in the $L^*$ values $a^*$ and $b^*$ values in the cementation of different cores, to the In-Ceram(P<0.01). $L^*$ values were not significantly different between the composite resin to the In-Ceram and the $a^*;b^*$ values were not significantly different between the amalgam and the non-precious alloy. 2. All of cementations of In-Ceram to the core materisal had color difference(${Delta}E^*ab$) compared to the In-Ceram. In the 0.3mm thickness of the In-Ceram copping non-precious alloy indicated the greatest value, while the composite resin core showed the lowest value with a thickness of 0.5mm In-Ceram copping. 3. By controlloing the In-Ceram coping thickness $L^*$ value was significatly different(P<0.01), but not in $a^*$ and $b^*$ values. 4. In an amalgam, precious & non-prcious alloys there was a 1,74 to 3.06 range color difference in the controlled thickness of In-Ceram coping at the thickness of 0.3mm and 0.5mm. The above results suggest that the requirement of the sufficient thickness of In-Ceram coping and the suitable core material in order to get an estheti restoration by In-Ceram and also to intercept the original core color.