The purpose of this study was to evaluate the shear bond strength between various resin-bonded retainers and enamel according to the adhesive resins and retention types and observe the bond filure modes with scanning electron microscope(SEM). For this purpose, the followin eight sub-groups were tested in shear bond strength : 1) electrochemically etched group(Verabond) using Panavia EX and Superbond C&B 2) tin-plated group(PG-S) using Panavia EX and Superbond C&B 3) salt-treated group(Verabond) using Panavia EX and Superbond C&B 4) meshtreated group(Verabond) using Panavia EX and Superbond C&B. Thermocycling test was conducted on the condition of 15 second dwell time each in $5^{circ}C$ and $55^{circ}C$bath. Shear bond strength was measured by Instron Universal Testing Machine(medel 1125). The obtained results were as follows : 1. After thermocycling, the shear bond strengths of tin-plated group and electrochemically etched group were significantly greater than those of salt-treated group and mesh-treated group. And the shear bond strength of Panavia EX was greater than that of Superbond C&B with salt-treated group and tin-plated group(p<0.05). 2. Before thermocycling, electrochemically etched group using Superbond C&B produced the greatest shear bond strength(p<0.01). 3. The shear bond strength of electrochemically etched group using Superbond C&B was significantly decreased after thermocycling(p<0.01). 4. In observation of bond failure modes before thermocycling, Panavia EX highly exhibited enamel fracture. Tin-plated group using Superbond C&B adhesive failure between metal and resin and electrochemically etched group using Superbond C&B exhibited adhesive failure between enamel and rdsin. 5. In observation of failure modes after thermocycling, Panavia EX exhibited cohesive failure and Superbond C&B exhibited adhesive failure between resin and metal.