This study was performed to evaluate effective surface conditioning method of In-Ceram core to improve bonding with resin cement. The surface of each sample was avraded with glass bead for 20 seconds and then subjected to one of the following conditions : no modification, sandblasting with $50{mu}m$ slumimum oxide powders for 20 seconds, etching with 20% hydrofluoric acid for 5, 10, and 15 minutes(half of the etched samples were coated with silane), and sandblasting with $250{mu}m$ aluminum oxide powders and silica coating whith Silicoater MD system(Kulzer, Germany). The surface morphology changes were examined with scanning electronic microscope(SEM. and the shear bond strength of In-Ceram core samples to resin cement(Panavis 21, Kurayay, Japan) were measured. It was concluded that : 1. By SEM observation, 20% HF acid etching did not create clear microretentive structure and surface roughness diminished with increace in etching time. Sandblasting was more effective than 20% hydrofluoric acid etching in producing microretentive structure. 2. The bond strengths of all In-Ceram core samples surface conditioned were increased that that of control group. 3. Silica coating showed higher bond strength than etching with 20% hydrofluoric acid. 4. The use of silane coating was more effective in improving bond strength than lengthening etching time.