Veneers of two nominal thicknesses, 1.5 and 2.5mm, were rotary peeled from Japanese larch (Larix leptolepis). Dahurian larch (Larix gmelinei) and Radiata pine (Pinus radiata) bolts unheated and heated in the water vat temperature of $66^{circ}C$ by rising a final temperature at 10cm core of $60^{circ}C$ to remain core diameter of 11.4cm. 1.5 and 2.5mm thick veneer cut from the heated Japanese larch were significantly thinner than those of the unheated bolt and 2.5mm thick veneer cut from the heated Dahurian larch were significantly thicker than that of the unheated bolt. 1.5mm thick Dahurian larch veneer and 1.5 and 2.5mm thick Radiata pine veneers showed insignificant difference between the unheated and heated bolts, respectively. Check distance on the loose side of 1.5mm thick veneer cut from the heated Radiata pine was significantly wider than that of the unheated bolt. However check distances on the loose side of 1.5 and 2.5mm thick Japanese larch and Dahurian larch veneers and 2.5mm thick Radiata pine veneers showed insignificant difference between the unheated and heated bolts. Also the depth of check on the loose side of three species showed insignificantly difference between the unheated and heated bolts. Arithmatic mean deviation($R_a$) and maximum height($R_{max}$) of the profile on the loose side of dried veneer by preheating the bolt compared with unheated bolts were different among apecies and between veneer thickness. The preheating treatment slightly affected qualities of these thin veneers such as 1.5 and 2.5mm. The yield of 2.5mm thick veneer from the heated radiata pine was significantly higher than that of the unheated bolt. However the yield of 2.5mm thick veneer for other two species and 1.5mm thick veneer for three species showed insignificant difference between the unheated and heated bolts. The yield of 2.5mm thick veneer for three species were higher than those of 1.5mm thick veneer. The average yields of green veneer of Japanese larch. Dahurian larch and Radiata pine were 57.1, 55.1 and 54.0 percent, respectively. Variables such as initial MC. drying time and veneer thickness had strong effect for Japanese larch veneer, less effect for Radiata pine veneer and nuch less effect on final MC for Dahurian larch veneer in jet drying. Correlation between the current MC and the drying time of Dahurian larch with low variation of initial MC was higher than those of Japanese larch and Radiata pine veneer with high variation of initial MC in high temperature drying. Thickness shrinkages of 2.5mm thick veneer for Japanese larch and Radiata pine were higher than those of 1.5mm thick veneers, but shrinkages of Dahurian larch veneer were similar between two nominal veneer thicknesses.