A residue from the newsprint waste was investigated as a filler in adhesive for bonding southern pine plywood. The residue was prepared by drying the wet residue to 8% moisture content and grinding the dry material using a laboratory Wiley mitt with a 75-${mu}m$(200-mesh) screen. The residue was compared to a commercial filler commonly used in structural plywood adhesives. A total of 48 three-ply panels. 12.7mm nominal thickness and 0.3 by 0.3 m in size, were fabricated at two press times(4 and 5 min) and three assembly times(20, 40 and 60 min). Evaluations of the residue were carried out by performance tension shear tests after two 4-hour boil accelerated aging tests on plywood. The test results included tension shear strength and estimated wood failure values. All plywood made with the residue filler were comparable to the control-bonded plywood. These results indicate that residue from the newsprint waste streams would be suitable as filler for plywood adhesives.