Polycrystalline $Sr_{2}(Ta_{1-x}Nbx)_{2}O_{7}$ and $La_{2}Ti_{2}O_{7}$ ceramics having very high Curie temperatures were synthesized by the conventional oxide mixing method (CON) and the molten salt synthesis method (MSS). Physical characteristics and phase relationship of calcined powders, as well as the sintering behavior, the grain-orientation and dielectric properties of sintered ceramics were investigated as a function of composition and firing temperature. The single $A_{2}B_{2}O_{7}$ phase was synthesized by using the MSS method at 100 - $150^{circ}C$ lower temperature compared to the CON method. As Nb content increased in $Sr_{2}(Ta_{1-x}Nbx)_{2}O_{7}$ ceramics, the Curie temperature and the dielectric constant at Curie temperature were raised, and the sintering behavior and the degree of grain-orientation were also improved at the same time. The use of MSS-derived powders made it possible to lower the sintering temperature and to improve the dielectric properties of the sintering samples. However, the piezoelectric properties as well as the grain-orientation were not improved any further by the MSS route.