In this paper dielectric and electrostrictive strain properties of (1-y-x)Pb(Mg$_{1/3}$Nb$_{2/3}$)O$_{3}$-PbTiO$_{3}$$-yPbTiO_{3}-xSrTiO_{3}[(1-y-x)PMN-yPT-xST]$ ceramics fabricated by using columbite precursor method have been investigated with the substitution of SrTiO$_{3}$(ST). Dielectric constant of the specimens increased with the increase of ST content up to 5[m/o] and decreased with further substitution of ST. And the pyrochlore phase decreased with the increase of ST content up to 5[m/o] in XRD analysis. The elimination of the pyrochlore phase improved dielectric constants. The electrostrictive strains generated by AC electric field have the highest value at 5[m/o] SrTiO$_{3}$ addition and the hysteresis of strain ranged from 12 to 20[%]. The electrostrictive strain at various temperature investigated in the temperature range of $-50[^{circ}C]~74[^{circ}C].$ In higher temperature than phase transition region, it showed paraelectric property which shows very small hystersis.