The breakdown characteristics of metal-oxide-semiconductor(MOS) capacitors fabricated by Al, polysilicon, and tungsten polycide gate electrodes onto gate oxide was evaluated by time zero dielectric breakdwon (TZDB). The average breakdown field of the gate oxide with tungsten polycide electride was lower than that of the polysilicon electrode. The B model (1~8MV/cm) failure of the gate oxide with tungsten polycide electrode was increased with increasing annealing temperature in the dry $O_{2}$ ambient. This is attributed ot fluorine and tungsten diffusion from thungsten silicide film into the gate oxide, and stress increase of tungsten polcide after annealing treatment.