Drilling tests were carried out austempered ductile castiron(ADI) to clarify the factors influencing the drilling characteristics of ADI material. The machinability of material was evaluated using high speed steel drill and cobalt contained drill of 6mm diameter. The spheroidal graphite cast iron materials were austenized at 90$0^{circ}C$ for 1 hour and then wear was kept at 375$^{circ}C$ for 2 hours. Austempered ductile cast iron contains a great deal of retaine austenite which contributes to an improvement of impact strength, In this paper, machinability of ADI was investigated by drilling experimentation. The results obtained are as follows: a)Flank wear increases logarithmically with the increases of cutting time. b) Relation of flank wear and cutting force can be appiled to $F_z$ = 925VB + 820 for the cutting suggested condition. c) Drilling hole number of about 2 times can be reduced more step feed than ordinary feed due to the high hardness of ADI material and hardness increasing ascribed to the martensite of retained austenite.